Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Industries
- Applications
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Typical Properties
Value Units Test Method / Conditions C14 Content min. 87 % ASTM D 6866 - Blown Film Properties
Value Units Test Method / Conditions Tensile Strength (at Break, MD) 50 MPa ASTM D882 Tensile Strength (at Break, TD) 40 MPa ASTM D882 Elongation (at Break, MD) 1130 % ASTM D882 Elongation (at Break, TD) 1430 % ASTM D882 Tensile Modulus (1% Secant, MD) 180 MPa ASTM D882 Tensile Modulus (1% Secant, TD) 200 MPa ASTM D882 Dart Drop Impact Strength 120 g/F50 ASTM D1709 Elmendorf Tear Strength (MD) 180 gF ASTM D1922 Elmendorf Tear Strength (TD) 400 gF ASTM D1922 Haze 12 % ASTM D1003 Gloss (Angle 60°) 48 % ASTM D2457 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 2.16kg) 1 g/10 min ASTM D1238 Density 0.916 g/cm³ ASTM D1505 - Note
Blown Film Properties:
- LDPE: 100 μm thick film, obtained from a 40 mm extruder, with blow up ratio of 2.2:1 (MD = Machine Direction and TD = Transversal Direction).
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards