Value Units Test Method / Conditions C14 Content min. 95 % ASTM D 6866 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 2.16kg) 0.34 g/10 min ASTM D1238 Density 0.956 g/cm³ ASTM D792 - Typical Properties - Plaque Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 21.6kg) 28 g/10 min ASTM D 1238 Tensile Strength (at Yield) ᵃ 30 MPa ASTM D 638 Tensile Strength (at Break) ᵃ 30 MPa ASTM D 638 Flexural Modulus (1% Secant) ᵇ 1250 MPa ASTM D 790 Tensile Impact Strength (at 23°C) 110 kJ/m² ISO 8256 Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 10% Igepal CO630) ᵃ 30 h/F50 ASTM D 1693 Deflection Temperature Under Load (at 0.455 MPa) ᵇ 70 °C ASTM D 648 Vicat Softening Temperature (at 10 N) ᵇ 127 °C ASTM D 1525 - Note
Typical properties correspond to average values obtained in our laboratories. Test specimens prepared from compression molded sheet made according to ASTM D 4703. Thickness of test piece: a) 2 mm; b) 3 mm.