Properties
- Typical Properties
Value Units Test Method / Conditions C14 Content min. 96 % ASTM D 6866 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 2.16kg) 2 g/10 min ASTM D 1238 Density 0.952 g/cm³ ASTM D 792 - Typical Properties - Plaque Properties
Value Units Test Method / Conditions Tensile Strength (at Yield) ᵃ 27 MPa ASTM D 638 Tensile Strength (at Break) ᵃ 36 MPa ASTM D 638 Flexural Modulus (1% Secant) ᵇ 1110 MPa ASTM D 790 Shore D Hardness ᶜ 62 - ASTM D 2240 Izod Impact Strength ᵇ 65 J/m ASTM D 256 Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 10% Igepal CO630) ᵃ 35 h/F50 ASTM D 1693 Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 100% Igepal CO630) ᵃ 65 h/F50 ASTM D 1693 Deflection Temperature Under Load (at 0.455 MPa) ᵇ 65 °C ASTM D 648 Vicat Softening Temperature (at 10 N) ᵇ 126 °C ASTM D 1525 - Note
Typical Properties - Plaque Properties:
- Test specimens from compression molded plaque according to ASTM D4703. Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards