Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Industries
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Blown Film Properties
Value Units Test Method / Conditions Tensile Strength (at Break, MD) ¹ 25 MPa ASTM D882 Tensile Strength (at Break, TD) ¹ 20 MPa ASTM D882 Elongation (at Break, MD) ¹ 380 % ASTM D882 Elongation (at Break, TD) ¹ 870 % ASTM D882 Dart Drop Impact Strength ¹ 64.0 g/F50 ASTM D1709 Elmendorf Tear Strength (TD) ¹ 56 gF ASTM D1922 Haze ¹ 8 % ASTM D1003 Gloss (Angle 60°) ¹ 76 % ASTM D2457 Flexural Modulus (1% Secant, MD) 70 MPa D 882 Flexural Modulus (1% Secant, TD) 70 MPa D 882 - Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 2.16kg) 8.3 g/10 min ASTM D1238 Density 0.918 g/cm³ ASTM D1505 - Note
- 1 LDPE: 25 μm thick film, obtained from a 75 mm extruder, with blow up ratio of 2:1, die gap 1 mm and Die rate 1,75 kg/h.cm (MD = Machine Direction and TD = Transversal Direction).
- 2 ND: Not Determined.
- 3 25 μm thick film, temperature: 38° C, 100% RH.
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards