Properties
- Physical Form
- Control Properties
Value Units Test Method / Conditions Melt Flow Rate (at 190°C, 5kg) 0.33 g/10 min ASTM D 1238 Melt Flow Rate (at 190°C, 21.6kg) 9.3 g/10 min ASTM D 1238 Density 0.952 g/cm³ ASTM D 792 - Typical Properties - Blown Film Properties
Value Units Test Method / Conditions Tensile Strength (at Break, MD) 85 MPa ASTM D 882 Tensile Strength (at Break, TD) 45 MPa ASTM D 882 Elongation (at Break, MD) 590 % ASTM D 882 Elongation (at Break, TD) 740 % ASTM D 882 Tensile Strength (at Yield, MD) 40 MPa ASTM D 882 Tensile Strength (at Yield, TD) 30 MPa ASTM D 882 Elongation (at Yield, MD) 15 % ASTM D 882 Elongation (at Yield, TD) 5 % ASTM D 882 Elmendorf Tear Strength (MD) 5 gF ASTM D 1922 Elmendorf Tear Strength (TD) 50 gF ASTM D 1922 Dart Drop Impact Strength 200 g/F50 ASTM D 1709/A Secant Modulus 1% (MD) 750 MPa ASTM D882 Secant Modulus 1% (TD) 870 MPa ASTM D882 Sealing Initial Temperature 125 °C Braskem Method - Note
Typical Properties - Blown Film Properties: Film with 12.5 microns produce in a 75mm extruder with 1.3 mm of die gap and a blow‐up ra o of 4.5:1